Zinc nitrate

Determination of Constant - Volume Combustion Energy for the Complexes of Zinc Nitrate with Four Amino Acids A Multifunctional Constant Volume Bomb for Combustion Study

硝酸锌与四种α-氨基酸配合物的恒容燃烧能测定（英文）一个多功能燃烧模拟实验装置

Using zinc nitrate as the starting material and ammonia and urea as precipitating agent , we prepared nano-ZnO powder by direct precipitation method and homogeneous precipitation method .

以硝酸锌为原料，氨水、尿素为沉淀剂，同时加入表面活性剂，采用直接沉淀法和均匀沉淀法制备了纳米ZnO粉体。

Fast Measurement of Zinc Nitrate and Impurities

快速测定硝酸锌原料中锌及其杂质含量的方法

This paper investigates reaction mechanism and electrochemical behavior of ZnO thin films deposited on transparent conducting glass from a simple aqueous zinc nitrate solution .

以透明导电玻璃（TCO）为衬底，用硝酸锌水溶液作为电解液，研究了阴极还原沉积ZnO薄膜的反应机理和电化学行为。

Zn-doped TiO2 microspheres have been synthesized by introducing a trace amount of zinc nitrate hexahydrate to the reaction system .

通过向反应体系引入微量硝酸锌的方法成功制备了一些列Zn掺杂的TiO2微球型颗粒。

Antiseptic Micromeritics Material was developed with Calcium Monohydrate Phosphate as carrier , appending silver nitrate 、 zinc nitrate 、 kronos .

运用磷酸氢钙作载体，硝酸银，硝酸锌作抗菌剂，外加不等量的二氧化钛，制成了吸附型的抗菌粉体。

Ni-Zn ferrites were prepared with the citrate precursor by self-combustion technique , using ferric citrate or ferric nitrate , nickel nitrate , zinc nitrate , citric acid as the starting materials .

以柠檬酸铁或硝酸铁、硝酸锌、硝酸镍和柠檬酸为原料，利用溶胶直接自蔓延燃烧反应成功制备了尖晶石结构的NiZn铁氧体粉末。

Nanon-sized ZnO powders with particle size of 25-80 nm were prepared by a method of reflux boiling with microwave heating using zinc nitrate and sodium hydroxide as the starting materials and triethanolamine as the surfactant .

以硝酸锌和氢氧化钠为原料，三乙醇胺为表面活性剂，采用微波加热沸腾回流，在不同的反应条件下制备出了平均粒径为25～80nm的纳米级ZnO粉体。

We report the synthesis on rod-like ZnO with different sizes via homogeneous precipitation from zinc nitrate and urea . It was found that zinc nitrate concentration and the reaction temperature were the key factors leading to the formation of rod-like ZnO .

采用均相沉淀法以硝酸锌和尿素为原料，在不加任何表面活性剂的条件下合成了尺寸不同的棒状ZnO，硝酸锌的浓度和反应温度是合成棒状ZnO的关键因素。

In this article , silver nitrate , copper nitrate , zinc nitrate were used for the preparation of single-ingredient , two-ingredient , three-ingredient antibacterial sol , the antibacterial sol was utilized to endue cotton fabrics with enduring antibacterial property ;

本文使用硝酸银、硝酸铜、硝酸锌三种物质制备抗菌溶胶，分别制备了单一组分、双组分和三组分的抗菌溶胶，利用抗菌溶胶整理棉织物，赋予织物耐久的抗菌性能；

The results show that the radius of water droplet of NP-9 / hexanol / heptane / zinc nitrate solution microemulsion at 308 K and 318 K is 1.86 nm and 2.33 nm respectively , and such microemulsion is a good medium for the synthesis of nanoparticles .

结果表明：NP-9/正己醇/正庚烷/硝酸锌溶液微乳液体系的水核半径在308K和318K分别为1.86nm和2.33nm，可以作为制备纳米粒子的微反应器。

The suitable preparation conditions were as follows : zinc nitrate and iron nitrate as the precursors , molar ratio of Zn / Fe 1:2 , ammonia as the precipitator , normal mixing manner of the precipitator , precipitation end-point pH 8.04 , and calcination temperature 450 ℃ .

最佳制备条件为以硝酸锌和硝酸铁为前驱体（Zn/Fe摩尔比为2：1），以氨水为沉淀剂（沉淀终点pH值为8.04），采用正加法，焙烧温度450℃，焙烧时间4h。

Thus the tin was released from the plating bath using 2.5 g ammonium fluoride as the releasing agent in a acetic-pyridine buffer solution of a pH value 5.5 , and then inversely titrated using zinc nitrate standard solution in the presence of xylenol orange as an indicator .

在pH值为5.5的醋酸吡啶缓冲溶液中，用2.5gNH4F解蔽，4滴XO、1mLCPB指示终点，锌盐返滴定镀液中的锡。

All the experimental results were demonstrated as follows : 1 . We report the preparation on urchin-like ZnO microspheres by thermal decomposition of hydrozincite . The hydrozincite was synthesized by homogeneous precipitation of zinc nitrate and urea in the presence of a nonionic surfactant polyethylene glycol .

研究结果如下：1.采用均相沉淀法以硝酸锌和尿素为原料，聚乙二醇为表面活性剂合成水锌矿，通过煅烧水锌矿制得了海胆状的ZnO微球。

Fractal Structure Formation of Zinc Hydroxide Nitrate under a Behenic Acid Langmuir Monolayer Combined with Ammonia Vapor Diffusion

山嵛酸Langmuir膜结合氨气扩散控制生长碱式硝酸锌的分形结构

The purer nanometer zinc oxide powders can be made from the zinc nitrate .

以硝酸锌为原料可得到纯度较高的纳米氧化锌。

The title ultrafine zinc phosphate crystal has been prepared based on zinc nitrate and phosphoric acid as raw materials , ammonia as precipitant at the presence of surfactant with an additional crystallization process .

以硝酸锌和磷酸为原料，氨水为沉淀剂，在表面活性剂存在下增加晶化工序，制备了超细磷酸锌晶体。

The measurement conditions and accuracy of the measurement technique of ICP-AES for the major composition zinc and impurities like Fe , Ca , Mg , and Na etc in zinc nitrate are investigated .

文章主要考察了ICP-AES法测定硝酸锌中主要成分Zn和杂质Fe，Ca，Mg和Na等元素的测定条件及方法的准确度和精密度。

To probe in the kinetic features of the growth of zinc oxalate nanoparticles , the radius of the water droplet of NP-9 / hexanol / heptane / zinc nitrate solution microemulsion was inspected through diluting method ;

为了研究纳米粒子生长的动力学特征，用稀释法求取了该过程所涉及的NP-9/正己醇/正庚烷/硝酸锌溶液微乳液体系的水核半径；

Nanometer zinc oxide powders have been synthesized by means of a novel , quick and simple combustion synthesis method using urea and Tri ( hydroxymethyl ) aminomethane as fuel and zinc nitrate as oxidant .

以尿素或三（羟甲基）氨基甲烷（THAM）为燃料，以硝酸锌为锌源和氧化剂，采用燃烧合成的方法制备了纳米氧化锌。